Optical attenuation filter

ABSTRACT

This invention relates to attenuation filters having absorbing thin film layers, which comprises gray metals or metal compounds. The attenuation filters offer significant advantages when used in optical communication systems wherein they are subjected to a relatively high flux of incident light. It was surprisingly discovered that particular thin film materials provide significant protection to the attenuating thin films layer thereby improving the temporal stability and power handling capacity over prior art devices.

BACKGROUND OF INVENTION

[0001] In an optical communications systems optical signals may be transmitted in free space, but are generally transmitted over optical waveguides, typically optical fibers. Since optical fiber transmission offers tremendous bandwidth and transmission rate advances over the transmission of electrical signals, conversion to electrical signals are avoided as much as possible by active optical processing such as optical amplification, switching and routing. It is usually desirable to avoid conversion of the signal to an electrical signals until they reach the target destination, where they are converted back to electrical signals representing digital data, voice or images in various analog formats.

[0002] In order to maximize the capacity of fiber optic communication systems many signal are simultaneously transmitted over the same fiber waveguides in a scheme known as wavelength division multiplexing or WDM. In WDM each discrete signal may correspond to a different wavelength of light, known as an optical channel. Various non-linear properties of optical glass, active and passive components in the optical system produce cross talk between the WDM optical signal channels. This “cross talk” is insignificant if the signal to noise ratio is high and the power levels of all optical channels are comparable.

[0003] The optical devices and interconnections in any route will result in signal losses, thus the signal power and signal to noise ratio of any optical signal can be expected to vary with the routing path. When the communication system is a network, optical channels are combined and routed together in common waveguides with signals from different sources, the power levels in each optical channels are likely to be different, in which case the “cross-talk” from the stronger channels will degrade the signal to noise ration in the weaker channels.

[0004] Degradation is avoiding by balancing signal power, such as by selectively attenuating the stronger signals. The level of attenuation may need to be varied as a network is modified, expanded or actively modified so as to accommodate the variation in communication traffic that can be expected with customer use and demand.

[0005] Thin film optical filters may be used to attenuate such optical signals. A thin film filter comprises one or more layers of material, each layer pre-selected for its optical properties, at a specific thickness to provide spectral control by interference phenomena arising from the interaction of light reflecting off the multiple thin film layers and/or absorption of energy by the thin film material.

[0006] Optical filters which utilize the inherent optical absorption of thin film materials are simpler in construction and avoid the characteristic reflected signal of an interference based filter, which must be managed to avoid cross talk or feedback to semiconductor lasers in the optical system. Although interference filter require more layers, they can be fabricated from dielectric materials having high stability to both environmental cycling of temperature and humidity as well as exposure to high optical powers.

[0007] Since an optical communications system must be highly reliable, yet adapted to variations in customer demand and utilization patterns, the ideal attenuation filter provides a reliably stable level of attenuation, preferably with a minimum attenuation variation, over all the signal channels in the WDM system.

[0008] Accordingly, it is an object of the present invention to provide an attenuating filter for optical communications systems that is stable over many years of use and provides uniform attenuation over a very broad wavelength range in a WDM system.

[0009] It is an additional object of the present invention to provide an attenuating filter and a method of adjusting the attenuation levels without sacrificing the uniform attenuation or low reflectivity a very broad wavelength range in a WDM system.

[0010] It is an additional object of the present invention to provide an attenuating filter and a method of adjusting the attenuation levels without sacrificing the uniform attenuation or low reflectivity a very broad wavelength range in a WDM system.

SUMMARY OF INVENTION

[0011] The attenuating filter provides both low reflectivity and uniform attenuation over the telecommunications C and L bands. The filter comprises a substrate, an attenuating coating deposited on at least a portion of the first surface of the substrate, a buffer coating deposited after the attenuating coating and has additional thin film layers to protect the attenuating coating from the environment and act as an antireflection coating on the clear locations on the substrate.

[0012] The attenuating filter preferably has a second antireflection coating deposited on the second surface of the substrate such that the reflectivity on the second surface of the attenuating filter is less than about 0.1 percent.

[0013] We have discovered that the appropriate selection of buffer layer and its incorporation within the antireflection coating design provides both the desired spectral control characteristics, but also has enhanced stability and resistance to degradation at high levels of incident light utilized in an optical telecommunications system.

[0014] These and other features, aspects, and advantages of the present invention will become better understood with reference to the following description and appended claims.

BRIEF DESCRIPTION OF DRAWINGS

[0015]FIG. 1 schematically illustrates the cross-section of a conventional attenuating filter.

[0016]FIG. 2 schematically illustrates the cross-section of one embodiment of the attenuating filter of the instant invention.

[0017]FIG. 3 schematically illustrates the cross-section of another embodiment of the inventiont where the attenuating layer thickness varies spatially across the surface of the filter.

[0018]FIG. 4 is a graph plotting the attenuation of the inventive filter as a function of wavelength.

[0019]FIG. 5 is a graph plotting the reflectivity of the second surface of the inventive filter as a function of wavelength.

DETAILED DESCRIPTION

[0020]FIG. 1 schematically illustrates a cross-section of a conventional attenuating filter. A thin film of metal 2 is deposited on an optically transparent substrate 1 at a thickness sufficient to produce the desired signal attenuation level by absorption of the incident radiation. Since metals are typically soft and can degrade in a typical operating environment, it is desirable to apply a protective layer over the metal. In cases where the film has a graded thickness as shown in FIG. 3, an antireflection coating 3 is applied to minimize the reflectivity from the un-coated section of the substrate. A conventional dielectric anti-reflection coating comprises one or more layers of the dielectric material having a thickness on the order of ¼ wavelength of the incident radiation intended to be reduced. In order to achieve low reflection over a broader range of wavelengths to the entire reflection coating may consist of multiple layers of dielectric material, the materials characterized by one material having a lower refractive index than the other material, which in the case of two dielectric materials is simply referred to as a high index material layer.

[0021]FIG. 1 follows the conventional teaching of optical thin film design that the high index layer is deposited on the metal layer, followed by a low index layer, followed by a second high index layer and terminating with a low index layer; wherein the optical thickness of each high and low index material is adjusted to minimize the reflection at the desired wavelengths.

[0022] We have discovered the performance attributes useful in an optical communication system are significantly improved by taking the opposite approach; depositing or placing the low reflective index layer on or proximate to the metallic layer.

[0023] In a preferred embodiment of the invention, schematically illustrated in FIG. 2, the materials and thickness correspond to the layers set forth in Table I. In this embodiment the dielectric thin film coatings can be characterized as an adhesion layer of any intermediate refractive index material (aluminum oxide) deposited on the metal layer (“INCONEL 600”), followed by the lower refractive index material (silicon dioxide) deposited on the intermediate refractive index material, followed by a high refractive index material (tantalum oxide), followed by a second low refractive index material (magnesium fluoride) having a lower refractive index than silicon dioxide. FIG. 4 illustrates the attenuation of light transmitted by the filter as a function of wavelength a 7 degree angle of incidence. The maximum variation from 15 dB, or ripple, is less than 0.02 dB. TABLE I Optical Thickness Physical Thickness Refractive Index Material (4nd), nm (d), nm (n) at 1550 nm Substrate (BK7 glass) — 1.48 “Inconel 600” not applicable from 0 to 100 nm n = 4.32, k = 6.4 Al₂O₃ 50 8 1.65 SiO₂ 1490 258 1.444 Ta₂O₅ 472 56 2.12 SiO₂ 849 145 1.444 Ta₂O₅ 1007 119 2.12 MgF₂ 1788.2 324 1.38

[0024] The use of two low refractive index materials, silicon dioxide and magnesium fluoride, was found to increase the wavelength range of the low reflectivity region such that the attenuating filter is suitable for both the telecommunication C and L bands. FIG. 5 illustrates the reflectivity of this surface as a function of wavelength. This particular design results a reflectivity of less than about 0.001 percent from between about 1472 to about 1660 nm. Similar coating designs using only silicon dioxide or magnesium fluoride will produce similar results.

[0025] Not wishing to be bound by theory, we believe a preferred layer for proximate contact or coverage of the attenuating layer of the filter is an oxide of silicon. The low index layer of an oxide of silica appears to provide a protective or buffering function such that thermo-oxidative degradations of the underlying attenuating layer is substantially reduced. In the context of an optical communication system, this stability of the attenuating material advantageously provides consistent attenuation level over the entire useful wavelength range, potentially minimizing the likelyhood of failure and device replacement for a period of many decades.

[0026] While the buffer layer is preferably an oxide of silicon, such as silicon monoxide, silicon dioxide, SiOx (wherein x is less than 2) and the like, other low refractive index compounds are also suitable, such as aluminum oxide, or mixtures of such compounds with oxides of silicon.

[0027] Accordingly, the low refractive index materials used in the construction of the dielectric anti-reflection coating, need not be limited to the combination of silicon dioxide and magnesium fluoride a shown in FIG. 2 and table I, but may include other relatively lower attractive index materials such as, aluminum oxide and the like, in varying combinations were any of these materials might be substituted for one or more of the multiple low refractive index layers.

[0028] The attenuating coating need not be limited to Inconel type alloys of nickel, but may comprise, nickel, chromium, tungsten, copper, gold, tantalum, iron and mixtures, alloys, or compounds thereof. Accordingly, the thickness of the attenuating layer would be adjusted correspondingly depending on the attenuation level sought to be achieved and the optical absorption characteristics of the attenuating coating.

[0029] Additionally, the high refractive index material utilized in the entire reflection coating need not be limited to a single material or tantalum oxide, but may utilize other relatively high refractive index optical coating materials for one or more of the high refractive index layers, such as hafnium oxide, niobium oxide titanium dioxide and the like.

[0030] Aluminum oxide is the currently preferred adhesion promoting layer for use in combination with the preferred attenuating layer materials, “INCONEL 600” alloy and silicon oxide buffer layer. Alternative adhesion promoting layers are as chromium, tantalum oxide, nickel oxide and zirconium oxide and other oxides of metals, which might be selected depending on the attenuating layer the level of adhesion required with a particular buffer layer in the application. Alternatively the substrate can be glass, fused silica and silicon and the like.

[0031] Any or all of the coating layers in the filter can be made by various methods of physical and chemical vapor deposition known to one of ordinary skill in the art of optical coating technology, including but not limited to, thermal evaporation, electron beam evaporation, ion assisted deposition, sputtering or chemical vapor deposition. However, it would be expected that the stability of the attenuating layer may still exhibit a relation to the composition of the attenuating layer and its inherent stability as well as film quality inherent in process used to produce the attenuating layer and the subsequently deposited layers in the filter construction.

[0032] Since a further objective of the invention is to minimize the total reflection from the attenuating filter the second surface of the substrate is preferably coated with an dielectric antireflection coating also having broad low reflection region as that illustrated in FIG. 5. Table II, below, provides details on the materials, design and construction of the anti-reflection coating on the second surface of the substrate. TABLE II Physical Optical Thickness Thickness Refractive Index (n), Material (4nd), nm (d), nm nm at 1550 nm Substrate — 1.52 (BK7 glass) Al₂O₃ 50 8 1.65 SiO₂ 1490 258 1.444 Ta₂O₅ 472 56 2.12 SiO₂ 849 145 1.444 Ta₂O₅ 1007 119 2.12 MgF₂ 1788.2 324 1.38

[0033] Variable Attenuating Filter

[0034] In a more preferred embodiment of the invention, the attenuating coating has a thickness variation across at least one dimension of the substrate such that the incident optical signal can be selectively attenuated by translating the attenuating filter parallel to the plane of the first surface of the substrate such that the incident signal is intersected by a thicker or thinner portion of the attenuating coating to produce or tune the desired level of signal attenuation.

[0035] Various methods of making filters having a variation in thickness of one or more layers, such as linearly or circular variable filters and alike, are known to those ordinary skill in the art of optical coating technology. For example U.S. Pat. No. 3,442,572, entitled Circularly Variable filter (Illsley, et al.) and U.S. Pat. No. 3,617,331, entitled Method for Manufacture of Rotatable Variable Filter (Illsley et al.), the disclosures of which are incorporated herein by reference, teach various methods in of manufacturing linearly variable filters by physical vapor deposition. U.S. Pat. No. 5,993,904, entitled Three-dimensional masking method for control of coating thickness, which is incorporated herein by reference, discloses chemical vapor deposition methods for producing and thin film coating having a controlled thickness distribution of various two-dimensional gradients.

[0036] Furthermore, the attenuation filter of the instant invention can be deployed within an optical communications system and adapted for either variable translation, to achieve various levels of attenuation in the case of filter having a spatial thickness variation in the attenuating layer, or discrete translation. Representative mechanical apparatus and optical systems for such uses are described in U.S. Pat. No. 5,506,731, entitled Device for Controllably Moving an Optical Element (Smiley) and U.S. Pat. No. 5,745,634, entitled Voltage Controlled Attenuator (Garret et al.), which are both incorporated herein by reference.

[0037] In many cases it may be desirable to be able to adjust the attenuation level from a minimum value near zero, limited only by the absorption inherent in the substrate and antireflection layers, to some greater value. Although this can be accomplished by completely removing the attenuating filter from the beam path, this may hinder achieving complete alignment when the attenuating filter is re-inserted into the beam path.

[0038] The attenuating filter in FIG. 3 a region on the substrate devoid of an attenuating layer enabling a continuous attenuation range downward from substantially 100% transmission without removal of the filter from the optical path. This region is formed by masking the area prior to depositing the attenuating layer deposition, which is removed before the buffer layer is deposited.

[0039] In the conventional design in FIG. 1 a high transmission coating free area can only be defined by removing the mask from substrate after depositing all the coating layers as these layer would decrease the total transmission by increasing the reflectivity of the reflecting layer for the substrate. Stripping the mask however also exposes the metal attenuating layer, making it more vulnerable to oxidation and degradation of optical performance. In contrast when the buffer layer and the substrate have substantially the same refractive index, such as with SiO2 and glass, the buffer layer surrounds and covers the attenuating layer entirely, thus avoiding the exposed edges that would result from a conventional design.

[0040] Stability

[0041] The stability of the inventive filter was compared to conventional filters using a high powered laser (up to about 250 mW) to accelerate the test, with the failure criteria of 0.5 dB increase in attenuation. The failure rate at high power levels provide an estimate of a power acceleration factor, which provides an comparative estimate of the failure rates of interest at the lower power levels more typically encountered in optical telecommunication systems. It was not practical to characterize the filter stability under standard operating conditions of 50 and 100 mW as this would require decades of testing.

[0042] Methods of testing are disclosed in IEC 62005-2, Committee draft 86B/1176/CD 1998-12: Example of quantitative assessment of reliability based on accelerated aging test- Part 2a: Temperature and humidity; steady state, which is incorporated herein by reference.

[0043] Samples corresponding to the filter in Table I were exposed to optical powers of 150, 200 and 250 mW using a 1550 nm laser source During this exposure the optical transmission was measured over time so that a time to failure (TTF), defined as a 0.5 dB decrease in optical attenuation, could be determined at each power level. When the change in transmission over was linear with time the TTF was determined by extrapolation to 0.5 dB. The time for 50% of the sample population to fail was determined by fitting TTF data set to a log-normal distribution of y as a linear function of x, to determine the Median Time to Failure (MTF):

y=xσ+In(MTF)  (equation 1)

[0044] wherein σ=dispersion parameter.

[0045] A power acceleration factor for each filter type was determined by the Arrhenius activation energy model for degradation, according to equation 2:

R=Ro×exp(Ea/KT)  (equation 2)

[0046] Where R=failure rate; Ro=constant; K=Boltzmann's constant (8.61×10−5 eV); T=Temperature (in Kelvin) and Ea=Activation energy, in eV.

[0047] Plotting the MTF against the reciprocal of the temperature in Kelvin confirmed the premise that the dominant mechanism is thermo-oxidation of the attenuating material, as it revealed the linear relationship between (1/T) and (Ea/k). Extrapolated to lower power levels predicted an MTF (0.5 dB increase in attenuation at 50 mW power) of 41.7 years for the novel filter design illustrated in FIG. 2 (corresponding to Table I), vs. 35.9 years for a filter corresponding to the conventional design described FIG. 1. 

We claim:
 1. An optical attenuation filter comprising: a. a substrate having a first surface and a second surface, b. an attenuating layer deposited on at least a portion of the first surface of said substrate, c. a buffer layer having a refractive index less than about 1.65 in optical communication with said attenuating layer, d. one or more additional layers in optical communication with said buffer layer, said one or more additional layers comprising a first layer having a refractive index greater than about 1.65 deposited onto said buffer layer whereby said buffer layer and said one or more additional coating layers comprise an antireflective coating for said attenuating layer to provide a low reflectivity wavelength band.
 2. The optical attenuation filter of claim 1 wherein the attenuating layer has a variation in thickness across at least one dimension of said substrate.
 3. The optical attenuation filter of claim 1 further comprising an adhesion promoting layer between said attenuating layer and said buffer layer.
 4. The optical attenuation filter of claim 1 wherein the variation in transmission is less than about 1.0% over the low reflectivity wavelength band. 5.The optical attenuation filter of claim 1 wherein the variation of transmission is less than about 0.5% over the low reflectivity wavelength band from 1525 to 1630 nm.
 6. An optical attenuation device comprising: a. an optical signal input port, b. an optical signal output port, c. An optical attenuation filter disposed between said input port and said output port, for intercepting an optical beam carrying one or more optical signal channels, said attenuation filter comprising, i. a substrate having a first and second surface; ii. an attenuating layer deposited on a least a portion of the first surface of said substrate; iii. a buffer layer having a refractive index less than about 1.65 in optical communication with said attenuating layer; iv. one or more additional layers in optical communication with said buffer layer, said one or more additional layers comprising a first layer having a refractive index greater than about 1.65 deposited onto said buffer layer; d. a translating stage supporting said optical attenuation filter wherein said translating stage is adapted for selective translation of said optical attenuation filter in a direction substantially parallel to the surface of said substrate.
 7. The optical attenuation device of claim 6 wherein the attenuating layer has a variation in thickness in a direction substantially parallel to the substrate surface.
 8. The optical attenuation device of claim 6 wherein the translating stage is adapted to translate said optical filter between a first portion of the first surface of said substrate that is substantially free of said attenuating layer and a second portion of the first surface of said substrate covered by said attenuating layer.
 9. The optical attenuation device of claim 8 wherein said buffer layer is disposed on the first portion of the first surface of said substrate that is substantially free of said attenuating layer.
 10. The optical attenuation device of claim 8 wherein said buffer layer substantially surrounds the portion of said attenuating layer which is not facing said substrate.
 11. The optical attenuation device of claim 6 further wherein said optical attenuation filter further comprises: one or more additional layers in optical communication with said buffer layer, said one or more additional layers comprising a first layer having a refractive index greater than about 1.65 deposited onto said buffer layer, whereby said buffer layer and said one or more additional coating layers comprise an antireflective coating for said attenuating layer to provide a low reflectivity wavelength band.
 12. The optical attenuation device of claim 6 further wherein said optical attenuation filter further comprises: one or more additional layers in optical communication with said buffer layer, said one or more additional layers comprising a first layer having a refractive index greater than about 1.65 deposited onto said buffer layer, whereby said buffer layer and said one or more additional coating layers comprise an antireflective coating for said attenuating layer to provide wavelength band of substantially uniform transmission.
 13. An optical attenuation filter comprising: a. a substrate having a first surface and a second surface, b. an attenuating layer deposited on at least a portion of the first surface of said substrate, c. a buffer layer having a refractive index less than about 1.65 in optical communication with said attenuating layer, d. one or more additional layers in optical communication with said buffer layer, said one or more additional layers comprising a first layer having a refractive index greater than about 1.65 deposited onto said buffer layer, wherein said buffer layer comprises a material selected from the group consisting of silicon monoxide, silicon dioxide, SiOx (wherein x is less than 2), aluminum oxide and mixtures thereof, whereby said buffer layer and said one or more additional coating layers comprise an antireflective coating for said attenuating layer and provide a wavelength band of substantially uniform transmission.
 14. The optical attenuation filter of claim 13 wherein said attenuating layer comprises a material selected from the group consisting of nickel, chromium, tungsten, copper, gold, tantalum, iron and mixtures, and combinations thereof.
 15. The optical attenuation filter of claim 13 further comprising an adhesion promoting layer between said attenuating layer and said buffer layer.
 16. The optical attenuation filter of claim 15 wherein said adhesion promoting layer comprises a material selected from the group consisting of aluminum oxide, chromium, tantalum oxide, nickel oxide, zirconium oxide and combinations thereof.
 17. The optical attenuation filter of claim 1 wherein said one or more additional layers comprises a second layer having a refractive index less than about 1.5.
 18. The optical attenuation filter of claim 1 wherein said one or more additional layers comprises a second layer having a refractive index less than about 1.4.
 19. The optical attenuation filter of claim 18 wherein said buffer layer has a refractive index less than about 1.5 and the second layer of said one of more additional layers has a refractive index less than about 1.4.
 20. The optical attenuation filter of claim 18 wherein said buffer layer comprises a an oxides of silicon.
 21. The optical attenuation filter of claim 18 wherein the second layer of said one of more additional layers comprises a metal fluoride. 